4140 Steel Heat Treatment Chart

But it should be tempered for any heavy use.

4140 steel heat treatment chart.

It can be formed using conventional techniques in the annealed condition. This leaves near full hardness. The chart below describes various types of tool steels their composition and appropriate heat treating applications. However the mechanical properties of this steel will be affected if it is welded in the heat treated condition and post weld heat treatment should be performed.

Heat to 845 to 900 c 1550 to 1650 f and hold for a period of time which depends on the thickness of the section. Aisi 4140 alloy steel can be welded using all conventional techniques. 2 fully hardened 4140 ranges from 54 to 59 hrc. Normalizing annealing hardening tempering spheroidization stress relief etc.

4140hw alloy steel technical data 4140hw meets aisi4140 standards and has improved hardenability and strength in heavier cross sections. From available data for an oil quenched inch diameter round part you will need to temper at approximately. 4140 steel round bar sheet plate heat treatment machinability. 1 4140 is an ok die steel but is not recommended for radical shaped dies such as narrow fullering crown and so on.

You find 4140hw in a. 3 tempering recommendations from the asm heat treaters guide for 4140 4142 is a minimum of 400 f. Steel composition harden f temper f anneal f normalize f quench. Since the 90 martensite hardness of rc 51 lies within the upper and lower hardness limits the 3 4 bar will fully harden to the center.

For 4140 steel the recommended heat treatment 1 consists of heating to austenitizing temperature typically 1570 f 855 c followed by oil quenching. Inspection of a jominy chart for 4140 which can be found in the sae handbook shows that for a jominy distance of 5 the lower hardness limit is rc 51 and the upper limit is rc 59. Din 1 7225 steel has high ductility. Tempering temperature of 4140 alloy steel can be from 204 649 c 400 1200 f after normalizing and oil quenching and the corresponding rockwell hardness can be obtained.

Alloy description timkensteel s 4140hw grade is a fine grained low alloy steel that offers optimum heat treat response in heavier cross sections. Heat treatment to 845 c slow cooling from 755 c at a rate of 14 c 25 f hour to 665 c or rapid cooling to 675 c for 5 hours isothermal annealing. At the annealed condition 1 7225 alloy tool steel has good machinability. Aisi 4140 alloy steel is heated at 845 c 1550 f followed by quenching in oil.

It is required more pressure or force for forming because it is tougher than plain.